| Alloy Grade | Chemical Composition | |||||
|---|---|---|---|---|---|---|
| China GB | USA UNS | EURO EN | JAPAN JIS | Cu % | Pb % | Zn % |
| H62 | - | - | C2801 | 60.5 - 63.5 | ≤0.02 | Balance |
| Density G/Cm3 | Conductivity %IACS | Thermal Conductivity W/(M.K) | Modulus Of Elasticity GPa | Specific Heat J/(G.K) | Thermal Expansion Coefcien 10⁻⁶/K | Cold-Workability | Machinability | Plating Capability | Hot Dip Tin Plating Property | Weldability | Anti-Corrosion |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 8.5 |
25
|
116
|
103
|
0.377
|
20.3
|
Excellent
|
Suitable
|
Excellent
|
Excellent
|
Good
|
Excellent
|
| Temper | HV Hardness | Tension test | Bend properties | |||
|---|---|---|---|---|---|---|
| MPa Tensile strength | Elongation % | Thickness mm | Bend angle | Bend radius | ||
| 060 | - | ≥275 | ≥35 | <1.6 | 180° or W | - |
| H01 | 75 - 125 | 325 - 420 | ≥30 | <1.6 | 180° or W | Thickness*0.5 times |
| H02 | 85 - 145 | 355 - 450 | ≥25 | <1.6 | 180° or W | Thickness*1 times |
| H04 | 105 - 175 | 410 - 540 | ≥15 | <1.6 | 180° or W | Thickness*1.5 times |
| H06 | 145 - 195 | 520 - 620 | - | <1.6 | 180° or W | - |
| H08 | 165 - 215 | 570 - 670 | - | <1.6 | 180° or W | - |
| Alloy Grade | Chemical Composition | |||||
|---|---|---|---|---|---|---|
| China GB | USA UNS | EURO EN | JAPAN JIS | Cu % | Pb % | Zn % |
| H70 | - | - | C2600 | 68.5 - 71.5 | ≤0.01 | Balance |
| Density G/Cm³ | Conductivity %IACS | Thermal Conductivity W/(M·K) | Modulus Of Elasticity GPa | Specific Heat J/(G·K) | Thermal Expansion Coefcien 10⁻⁶/K | Cold-Workability | Machinability | Plating Capability | Hot Dip Tin Plating Property | Weldability | Anti-Corrosion |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 8.5 | 26 | 120 | 110 | 0.377 | 19.9 | Excellent | Suitable | Excellent | Excellent | Good | Excellent |
| Temper | HV Hardness | Tension test | Bend properties | |||
|---|---|---|---|---|---|---|
| MPa Tensile strength | longation % | Thickness mm | Bend properties - Bend angle | Bend properties - Bend radius | ||
| 060 | - | ≥275 | ≥35 | <2.0 | 180° or W | - |
| H01 | 75 - 125 | 325 - 420 | ≥30 | <2.0 | 180° or W | Thickness*0.5 times |
| H02 | 85 - 145 | 355 - 450 | ≥25 | <2.0 | 180° or W | Thickness*1 times |
| H04 | 105 - 175 | 410 - 540 | ≥15 | <2.0 | 180° or W | Thickness*1.5 times |
| H06 | 145 - 195 | 520 - 620 | - | <2.0 | 180° or W | - |
| H08 | 165 - 215 | 570 - 670 | - | <2.0 | 180° or W | - |
| Alloy Grade | Chemical Composition | |||||
|---|---|---|---|---|---|---|
| China GB | USA UNS | EURO EN | JAPAN JIS | Cu % | Pb % | Zn % |
| H62 | - | - | C2801 | 60.5 - 63.5 | ≤0.02 | Balance |
| Density G/Cm³ | Conductivity %IACS | Thermal Conductivity W/(M·K) | Modulus Of Elasticity GPa | Specific Heat J/(G·K) | Thermal Expansion Coefcien 10⁻⁶/K | Cold-Workability | Machinability | Plating Capability | Hot Dip Tin Plating Property | Weldability | Anti-Corrosion |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 8.5 | 24 | 116 | 103 | 0.377 | 20.3 | Excellent | Suitable | Excellent | Excellent | Good | Excellent |
| Temper | HV Hardness | Tension test | Bend properties | |||
|---|---|---|---|---|---|---|
| MPa Tensile strength | Elongation % | Thickness mm | Bend angle | Bend radius | ||
| 060 | ≤95 | ≥290 | ≥35 | ≥2.0 | 180° | - |
| H02 | 90 - 130 | 350 - 470 | ≥20 | ≥2.0 | 180° | Thickness*1 times |
| H04 | 125 - 165 | 410 - 630 | ≥10 | ≥2.0 | 180° | Thickness*1.5 times |
| H06 | ≥155 | ≥585 | ≥2.5 | ≥2.0 | 180° | - |